Bright Annealing Cold Rolled Stainless Steel Sheet 2B BA Finish 2mm
More informations of our products
Product name |
cold rolled hot rolled ASTM 201 304 316 Stainless Steel Sheet |
Specification |
410 2B: Thickness 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm 2.0mm 2.5mm 3.0mm. Standard Size: 1219 x 2438mm |
410 BA: Thcikness : 0.3mm 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm 2.0mm 2.5mm, Standard Size: 1250 x 2500mm |
Standard |
ASME, ASTM, EN, BS, GB, DIN, JIS, etc |
Finish |
NO.4, 2B, BA, HL, 8K, Mirror finish and so on |
Main Material |
201, 202, 304, 304L, 310S, 316, 316L, 410, 420, 430, 441, 2205,2507, 904L |
Brand Name |
TISCO, Baosteel, LISCO, JISCO |
Place of Origin |
Jiangsu of China (Mainland) |
Technical treatment |
Cold Rolled, Hot Rolled |
Port of Loading |
SHANGHAI |
Terms of Delivery |
FOB, CFR, CIF, CNF, EXWORK |
Terms of Payment |
L/C, T/T (30% desipot) |
Packing |
Standard export sea-worthy packing |
Delivery time |
Within 7-15 days after recieve 30% desipot or as your requirement |
Stock |
Ready in stocks |
About Our 410 Stainless Steel
Type 410 is a martensitic stainless steel which is magnetic, resists corrosion in mild environents and has fairly good ductility. 410 pipe is used where abrasion and wear resistance is needed, combined with fair resistance to general corrosion and oxidation.
Chemical Composition - Stainless Steel 410
Carbon Max |
.08-.015 |
Manganese Max |
1 |
Phosphorous Max |
0.04 |
Sulfur Max |
0.03 |
Silicon Max |
1.0 |
Chromium Range |
11.5-13.5 |
Nickel Range |
.75 |
Iron |
Balance |
Advance of Stainless Steel 410
Martensitic stainless steel with high mechanical properties.
Ferromagnetic in the annealed or hardened condition.
Contains minimum amount of chromium to impart stainless steel properties.
Resists oxidation and scaling up to 1200°F.
Resists abrasion and wear better than most 300 series stainless steels.
Good sulphide stress corrosion cracking resistance.
Hardness is one of Type 410's best features.
Mechanical properties of grade 410 stainless steels
Tempering Temperature (°C) |
Tensile Strength (MPa) |
Yield Strength 0.2% Proof (MPa) |
Elongation (% in 50mm) |
Hardness Brinell (HB) |
Impact Charpy V (J) |
Annealed * |
480 min |
275 min |
16 min |
- |
- |
204 |
1475 |
1005 |
11 |
400 |
30 |
316 |
1470 |
961 |
18 |
400 |
36 |
427 |
1340 |
920 |
18.5 |
405 |
# |
538 |
985 |
730 |
16 |
321 |
# |
593 |
870 |
675 |
20 |
255 |
39 |
650 |
300 |
270 |
29.5 |
225 |
80 |
Applications of 410 stainless steel
Bolts, screws, bushings and nuts
Petroleum fractionating structures
Shafts, pumps and valves
Mine ladder rungs
Gas turbines